Plus Silicon
• RTV-2310 silicone TECHNICAL INFORMATION
• Color: White
• tack: 1.8 mPa.s
• Gel time of 10 min to become
• Maintenance, storage, curing 60 min
• Hardness: 11 Jisan
• Life: 15 times
• tear strength endurance, strength: 7N/mm
• tensile strength: 18mpa
• Strain rate: 350%
GENERAL FEATURES
PLUS RTV2 mold used to receive two component is an elastomer at room temperature
vulkanize is vulcanized.
Mold-making techniques to the success of all the features listed below must be provided by the material. RTV2 of these features are all available.
Flexibility
- Sticking to the mold removal easy
- The fine detail reproduction accuracy up to
- High tear resistance
- Removing the heat released, the environmental temperature vulcanization (polymerization)
- Easy to use without requiring special equipment
- Lean
- High temperature resistance
- Dielectric properties
- Very low shrinkage, shrinkage rate of the two components are mixed vulcanization begins. Ideal conditions for vulcanization:
- 23 ° C surrounding temperature
- 50% relative humidity
In practice, dimensional accuracy is important if:
- Ambient temperature of 23-30 ° C to provide
- In no event shall not fall below 20 ° C,
- The minimum relative humidity of 30% of the work in atmospheric conditions,
- The need to stay loyal to the recommended dosage of catalyst.
• Color: White
• tack: 1.8 mPa.s
• Gel time of 10 min to become
• Maintenance, storage, curing 60 min
• Hardness: 11 Jisan
• Life: 15 times
• tear strength endurance, strength: 7N/mm
• tensile strength: 18mpa
• Strain rate: 350%
GENERAL FEATURES
PLUS RTV2 mold used to receive two component is an elastomer at room temperature
vulkanize is vulcanized.
Mold-making techniques to the success of all the features listed below must be provided by the material. RTV2 of these features are all available.
Flexibility
- Sticking to the mold removal easy
- The fine detail reproduction accuracy up to
- High tear resistance
- Removing the heat released, the environmental temperature vulcanization (polymerization)
- Easy to use without requiring special equipment
- Lean
- High temperature resistance
- Dielectric properties
- Very low shrinkage, shrinkage rate of the two components are mixed vulcanization begins. Ideal conditions for vulcanization:
- 23 ° C surrounding temperature
- 50% relative humidity
In practice, dimensional accuracy is important if:
- Ambient temperature of 23-30 ° C to provide
- In no event shall not fall below 20 ° C,
- The minimum relative humidity of 30% of the work in atmospheric conditions,
- The need to stay loyal to the recommended dosage of catalyst.